We are manufacturing, exporting and supplying the best quality Ladle Covering Compound. Our Laddle Covering Compound is made as per quality standards using Almina and Riceflakes. Laddle Covering Compound is free flowing in nature and used in tundish or ladle. Our Laddle Covering Compound reduces ladle jamming and heat loss due to radiation. Along with this, Laddle Covering Compound prevents contact of molten steel to the atmosphere.
Raw Material Used
Nozzle Filling Compound needed for steel transfer ladle with slide gate system. As Nozzle Filling Compound possesses selected granulometry and high refractoriness, it does not sinter when in contact with molten steel around 1600 oC temperature with high ferrostatic head when kept in ladle nozzle-well cavity. Thus, it results into free flowing when slide gate is opened and it comes out freely or with minor oxygen lancing establishing a very smooth stream from the ladle. Depending on nozzle diameter as well as holding time of molten metal in ladle, granulometry of Nozzle Filling Compound and chemical composition of refractory filler change.
Available In Three Types
Product : Mortar90k
ProductClass : Refractory Monolithic
Type : High Alumina Dense Castable
Nature Of Bond : Hydraulic
Installation : Vibration Casting
Maximum Service Temperature : 1800 0C
Maximum Grain Size : 0 – 0.10 mm
Water Required for Casting : 8.0-10.0%
Chemical Analysis, %
|Al2o3||88.00 – 89.00||88.5|
|Fe2o3||0.25 – 0.30||0.3|
|Dry density, g/cc % Retained Maximum Size||0-5||0.8|
Thermal Properties Analysis
|Refractoriness, Orton/ 0c||88.00 – 89.00||88.5|
Storage Life : Best Till 9 Months From The Date of Production if Stored In Proper Condation.